Publisher's Synopsis
Strainrange partitioning (SRP) was originally developed on an inelastic strain basis for isothermal fatigue in the high-strain regime where the inelastic strainrange could be determined accurately. However, most power-generating equipment operates in the regime where the inelastic strains are small and difficult to determine with any degree of accuracy. This shortcoming led to the development of the total strain version of SRP (TS-SRP). Power-generating equipment seldom operates under isothermal conditions, and isothermal life prediction methods cannot be depended on to predict the lives of anisothermal cycles. To overcome this shortcoming, a method was proposed for extending TS-SRP to characterize anisothermal fatigue behavior and to predict the lives of thermomechanical fatigue (TMF) cycles using apppropriate anisothermal data. The viability of this method, referred to as TMF/TS-SRP, was demonstrated using TMF data for two high-temperature aerospace alloys. In this report, data from the literature are used to examine the ability of TMF/TS-SRP to characterize the failure and flow behavior of three low-strength, high-ductility alloys widely used for ground-based power-generating equipment. The three alloys are type 304 stainless steel, 1Cr-1Mo-0.25V steel, and 2.25Cr-1Mo steel. Because of the limited nature of the data, it was possible to evaluate the characterization, but not the predictive capability of TMF/TS-SRP. Saltsman, James F. and Halford, Gary R. Langley Research Center RTOP 505-63-5B